Crusher Blow Bars / Impact Plates

OEM tailor design

Product name: Blow Bars 、Impact Plates、Impact Crusher hammer

Production process: Casting

Applicable machines: Various models of Impact Crushers

Material types: High manganese steel, high manganese steel inlaid alloy rod, Ceramic metal composite,bimetal composite, high chromium cast iron, alloy steel, etc.

Applicable industries:mining, cement plants, coal, steel, etc.

Our service:

1. Before sales, we will fully understand the customer's working conditions and recommend the most appropriate material selection to the customer.

2. Provide customers with drawings based on their machine models, spare parts dimensions, etc.

3. After sales, we will continue to pay attention to the usage of the product and provide timely help.

The materials of high manganese steel blow bars include Mn13Cr2, Mn18Cr2, Mn13 or Mn18 inlaid tungsten-molybdenum alloy rods and surface surfacing wear-resistant alloys.

Features: Applicable working conditions:suitable for cement plant, poor rock conditions such as send factory.

Applicable working conditions: Suitable for cement plant, poor rock conditions such as send factory.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	S	P
ZG120Mn13	1.05~1.35	0.3~0.9	11~14	-	≤0.06	≤0.04
ZG120Mn13Cr2	1.05~1.35	0.3~0.9	11~14	1.5~2.5	≤0.06	≤0.04
ZG120Mn17Cr2	1.05~1.35	0.3~0.9	16~19	1.5~2.5	≤0.06	≤0.04
1：Allowed to add microscale V,Ti,B and Re etc. 2：We can produce the other grade high manganese steel hammer according to customers’ requirments 。

Mechanical Property

Grade	Stretch property				Hardness HB
Grade	yield strength ReH/Mpa	tensile strength Rm/Mpa	Elongation at cross section %	Shock absorption energyKu2J	Hardness HB
ZG120Mn13	-	≥685	≥25	≥118	≤300
ZG120Mn13Cr2	≥390	≥735	≥20	-	≤300

We use proper alloying and and related technological measures to make High chromium iron blow bars’surface hardness reaches more than 58HRC , during the process of wearing will maintain high hardness and high wear resistance.

Applicable working conditions: Suitable for making wearable spare parts with lower impact load and simpler shape.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	Mo	Ni	Cu	S	P
BTMCr15	2.0~3.3	≤1.2	≤2.0	14~18	≤3.0	≤2.5	≤1.2	≤0.06	≤0.10
BTMCr20	2.0~3.3	≤1.2	≤2.0	18~23	≤3.0	≤2.5	≤1.2	≤0.06	≤0.10
BTMCr26	2.0~3.3	≤1.2	≤2.0	23~30	≤3.0	≤2.5	≤2.0	≤0.06	≤0.10
1：Allowed to add microscale V,Ti,Nb,B and Re etc. 2：We will choose grade and specific component according to blow bars’ weight ,thickness and sizes

Mechanical Property

Grade	Surface Hardness
	Casting condition		Harded condition		Softening annealing condition
	HRC	HB	HRC	HB	HRC	HB
BTMCr15	≥46	≥450	≥58	≥650	≥41	400
BTMCr20	≥46	≥450	≥58	≥650	≥41	400
BTMCr26	≥46	≥450	≥58	≥650	≥41	400
1：There are no exact corresponing value between rockwell hardness(HRC) and brine hardness(HB),so ,this two kind of hardness value can be inspend used 。 2：The hardness in the 40%deepness of casting section should be lower than 92% hardness of surface.

In the process of using ceramic blow bars, because ceramic high chromium cast iron have excellent wear resistance that other wear-resistant materials can not match, it greatly reduces the consumption of user materials and the labor cost of replacing wear-resistant parts, and becomes the representative of a new generation of wear-resistant materials.

Blow Bars

Crusher Blow Bars / Impact Plates

Related products

Hammer Crusher Rotor

Crusher Grate Plate/Mill Grate

Clinker Crusher Hammer

Raw Material Crusher Hammer

Cone Crusher Mantle/Bowl Liner

Crusher Blow Bars / Impact Pla

Jaw Plates

Crusher Hammer Heads

Crusher Liners/Mill liners

Quick Contact