Diaphragm For Mill_Zhili New Materials

The barrel is divided into intermediate baffles of two or three grinding bins. Theseparating wearhouse plate has holes that are smaller than the diameter of the steel balls in the two abrasive cavities to allow the material to pass through and be further milled. Due to long-time friction between steel balls and materials in the two sides of the abrasive silo, the silo panel needs to be very wear-resistant to shorten the replacement cycle. Some ball mills use double-layered diaphragms to better distinguish the two abrasive cavities and prevent them from collapsing and damaging the body.

Diaphragm For Mill 01.jpg

Diaphragm For Mill 02.jpg

Feature:

We use proper alloying and and related technological measures to make the blow bars’ surface hardness reaches more than 58HRC , during the process of wearing will maintain high hardness and high wear resistance.

Technology process

In blow bars’ working part we use the technique of directional solidification to make Cr7C3 type carbide is perpendicular to the part.The macro-hardness and micro hardness of carbide can be improved without reducing thoghness.

Application

Suitable for making wearable spare parts with lower impact load and simpler shape.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	Mo	Ni	Cu	S	P
BTMCr15	2.0~3.3	≤1.2	≤2.0	14~18	≤3.0	≤2.5	≤1.2	≤0.06	≤0.10
BTMCr20	2.0~3.3	≤1.2	≤2.0	18~23	≤3.0	≤2.5	≤1.2	≤0.06	≤0.10
BTMCr26	2.0~3.3	≤1.2	≤2.0	23~30	≤3.0	≤2.5	≤2.0	≤0.06	≤0.10
1：Allowed to add microscale V,Ti,Nb,B and Re etc. 2：We will choose grade and specific component according to blow bars’ weight ,thickness and sizes

Mechanical Property

Grade	Surface Hardness
	Casting condition		Harded condition		Softening annealing condition
	HRC	HB	HRC	HB	HRC	HB
BTMCr15	≥46	≥450	≥58	≥650	≥41	400
BTMCr20	≥46	≥450	≥58	≥650	≥41	400
BTMCr26	≥46	≥450	≥58	≥650	≥41	400
1：There are no exact corresponing value between rockwell hardness(HRC) and brine hardness(HB),so ,this two kind of hardness value can be inspend used 。 2：The hardness in the 40%deepness of casting section should be lower than 92% hardness of surface.

Feature

High manganese steel refers to high alloy steels containing more than 10% manganese. The biggest features of high-manganese steel are:

The greater external compressive stress or impact load, the more conducive to the formation of hardened layer, so the higher the wear resistance of the casting;

With the gradual wear of the hardened layer, new work hardened layers will continue to form under the influence of external compressive stress or impact loads. Therefore, it is suitable for making wearable spare parts that are subject to high impact load and wear for a long time, and is widely used in metallurgy, mining, building materials, railways, electric power, coal and other broken grinding equipment.

Chemical component

Grade	Chemical component %
Grade	C	Si	Mn	Cr	S	P
ZG120Mn13	1.05~1.35	0.3~0.9	11~14	-	≤0.06	≤0.04
ZG120Mn13Cr2	1.05~1.35	0.3~0.9	11~14	1.5~2.5	≤0.06	≤0.04
ZG120Mn17Cr2	1.05~1.35	0.3~0.9	16~19	1.5~2.5	≤0.06	≤0.04
1：Allowed to add microscale V,Ti,B and Re etc. 2：We can produce the other grade high manganese steel hammer according to customers’ requirments

Mechanical Property

Grade	Stretch property	Hardness HB
ZG120Mn13	-	≥685	≥25	≥118	≤300
ZG120Mn13Cr2	≥390	≥735	≥20	-	≤300

Grade

Stretch property

Hardness

yield strength ReH/Mpa

tensile strength Rm/Mpa

Section elongation%

impact absorbing energyKu2J

ZG120Mn13

≥685

≥25

≥118

≤300

ZG120Mn13Cr2

≥390

≥735

≥20

≤300

Feature

The alloy structure cast steel is an iron-carbon alloy formed by adding an appropriate amount of one or more alloy elements on the basis of ordinary carbon steel.

Process technology

According to the different elements added, with appropriate smelting and heat treatment process to obtain high strength, high toughness, high wear resistance, corrosion resistance, low temperature resistance, high temperature resistance, non-magnetic and other related special properties.

Scope of application

It is suitable for producing the wear-resisting spare parts with good mechanical strength and good toughness that are required for various working conditions, and the main steel structure castings with the required dynamic load.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	Mo	S	P	Ai
ZG42CrMo	0.38-0.43	0.15-0.35	0.75-1.00	0.80-1.10	0.15-0.25	<0.04	<0.035	-
ZG35CrMo	0.32~0.40	0.17~0.37	0.40~0.70	0.80~1.10	0.15~0.25	≤0.035	≤0.035	-
ZG38CrMoAl	0.35~0.42	0.20~0.45	0.30~0.60	1.35~1.65	0.15~0.25	≤0.04	≤0.04	0.7~1.1
ZG40Cr	0.37~0.45	0.17~0.37	0.5~0.8	0.8~1.1	-	-	-	-
ZG30Mn2SiCrMo	0.25~0.35	0.40~0.80	1.20~1.60	1.35~1.65	0.2~0.5	≤0.04	≤0.04	-

Mechanical Property

Grade	tensile strength（Mpa）	yield strength （Mpa）	Elongation at cross section（%）	Section shrinkage rate（%）	Shock absorption energy（KV2/J）
ZG42CrMo	≥1080	≥930	≥12	≥20	≥24
ZG35CrMo	≥985	≥835	≥12	≥20	≥24
ZG38CrMoAl	≥980	≥835	≥14	≥20	≥24
ZG40Cr	≥980	≥785	≥9	≥20	≥24
ZG30Mn2SiCrMo	≥1500	≥1300	≥3	-	≥24

Diaphragm For Mill/Separating Wearhouse Plate

Related products

Hammer Crusher Anvil

Alloy stud surfacing welding roller

Wear liner plates for chutes

Crusher Rotor

Crusher Grate Plate/Mill Grate Plate/Diaphragm

Clinker Crusher Hammer

Raw Material Crusher Hammer

Cone Crusher Mantle/Bowl Liner/Concave

Crusher Blow Bars

Quick Contact